Diesel Resistant Neoprene Heat Shrinkable Tubing



Diesel Resistant Heat Shrink Tubing

 is made of high-quality Chlorinated Polyolefin material, featuring a 2:1 shrink ratio. It offers exceptional resistance to fuel, diesel, lubricating oil, chemical corrosion, abrasion, and flame. Moreover, it maintains flexibility even in low-temperature environments. This tubing is compliant with RoHS and REACH environmental regulations, making it suitable for a wide range of applications in commercial, military, and aerospace industries. Whether for wire insulation, stress relief, or friction protection, our Diesel Resistant Heat Shrink Tubing provides reliable performance and durability.


  • Material:Chloroprene Rubber, Neoprene
  • Opeating Temeraturerange:-70℃~121℃
  • Minimum shrink temperature:90℃
  • Minimum fully recovery temperature:135℃
  • Color:Black


Property Requirement Test method Typical data
Longitudinal shrinkage ≤10% ASTM D2671 ≤5%
Tensile strength 10.3MPa min. ASTM D638 ≥11 MPa
Elongation at break 225% min. ASTM D638 ≥300%
Tensile strength after ageing(121℃ * 168hrs) 8.2MPa min. ASTM D638 ≥10.4 MPa
Elongation after ageing(121℃ * 168hrs) 175% min. ASTM D638 ≥200%
Heat shock(150℃ * 4hrs) No crack ASTM D2671 No crack
Low-temperature flexibility(-70℃ * 4hrs) No crack ASTM D2671 No crack
Dielectric voltage withstand 2000V,60sec,No breakdown ASTM D2671 No breakdown
Dielectric strength 11.8 KV/mm min. ASTM D2671 ≥15 KV/mm
Volume resistivity 10 11 Ω·cm min. ASTM D876 ≥10 11 Ω·cm
Corrosion No corrosion ASTM D2671 No corrosion
Flammability Self-extinguishing within 15s ASTM D2671 Pass
Fluids resistance(23℃ * 24hrs)
Tensile strength 6.9 MPa min. ASTM D638 ≥9.0MPa
Elongation at break 175% min. ASTM D638 ≥200%
Dielectric strength 9.8 KV/mm min. ASTM D2671 ≥12 KV/mm

Engineering Picture

Good Gi -Diesel Resistant Neoprene Heat Shrinkable Tubing-size


{{ typeOne.merge }}
{{ itemOneTitle }}
{{ item }}


{{ typeTwo.merge }}
{{ itemTwoTitle }}
{{ item }}
{{ typeThree.merge }}
{{ itemThreeTitle }}
{{ item }}